Epoxy composites filled with high surface area-carbon fillers
2013
Citation: J. Appl. Phys. 114, 164304 (2013); doi: 10.1063/1.4826529 (Received 24 July 2013; accepted 6 October 2013; published online 22 October 2013) A comprehensive analysis of electrical, electromagnetic (EM), mechanical, and thermal properties of epoxy resin composites filled with 0.25–2.0 wt. % of carbon additives characterized by high surface area, both nano-sized, like carbon nanotubes (CNTs) and carbon black (CBH), and micro-sized exfoliated graphite (EG), was performed. We found that the physical properties of both CNTs- and CBH-based epoxy resin composites increased all together with filler content and even more clearly for CBH than for CNTs. In the case of EG-based composites, go…
Steady and oscillatory shear behaviour of semi-concentrated starch suspensions
2011
The viscoelastic moduli G’ and G” of aqueous suspensions with 40% (w/v) normal corn starch (NCS) and waxy corn starch (WCS) were determined by oscillation rheometry. The oscillatory shear flow experiments at heating from 30° to 75 °C and maintaining at this temperature showed changes from a behaviour predominant viscous (G”>>G’) to predominant elastic (G’>G”) for both starches at 60.5 °C for WCS, respectively 70,85 °C for NCS, WCS having higher values of G’ and G” as NCS. After the gelatinisation temperature was attired, NCS showed no significant changes, both moduli remaining relatively constant. Peaks of both moduli G’ and G” were obtained for WCS at its maintaining at 75oC, these changes…
Comparison of mechanical properties and composition of magnetron sputter and plasma enhanced atomic layer deposition aluminum nitride films
2018
A comparative study of mechanical properties and elemental and structural composition was made for aluminum nitride thin films deposited with reactive magnetron sputtering and plasma enhanced atomic layer deposition (PEALD). The sputtered films were deposited on Si (100), Mo (110), and Al (111) oriented substrates to study the effect of substrate texture on film properties. For the PEALD trimethylaluminum–ammonia films, the effects of process parameters, such as temperature, bias voltage, and plasma gas (ammonia versus N2/H2), on the AlN properties were studied. All the AlN films had a nominal thickness of 100 nm. Time-of-flight elastic recoil detection analysis showed the sputtered films t…
Benchmark study of undrained triaxial testing of Opalinus Clay shale: Results and implications for robust testing
2021
Triaxial testing of argillaceous rocks and shales is significantly more challenging than conventional rock mechanical testing. The challenges are mainly related to the very low permeability of these geomaterials, and their sensitivity to exposure of atmosphere and brines, which induces variations of water content, suction and effective stress. There are currently no international standards to guide service laboratories for robust testing procedures for shales. A benchmark study of undrained triaxial testing was therefore initiated with three leading service laboratories in shale testing, performing 13 tests and using two different methods of establishing sample saturation prior to deformati…